- High filler ratio (73 wt%) helps to reduce volumetric shrinkage (3.5 %) and shrinkage stress while increasing compressive and flexural strength
- Vickers Hardness test results (48 Hv) show above 95 % polymerization at 4mm depth of cure
- High flexural strength (119 Mpa) with a low flexural modulus (9 Gpa)
- Natural Opaque shade stability to match surrounding tooth structure
- Superior fluoride release and rechargeability
- Self-leveling allows easy adaptation
- 10 second cure time
- High level of radiopacity, 2.5 Al:mm